Medium-long wavelength infrared quantum cascade laser of MOCVD on silicon

830
2023-08-04 16:26:34
Δείτε τη μετάφραση
Us researchers report 8.1 μm wavelength quantum cascade laser (QCL) grown on silicon (Si) by MOCVD [S. Xu et al., Applications. Physics Letters, v123, p031110, 2023]. "There are no previous reports of QCL growth on silicon substrates by metal-organic chemical vapor deposition (MOCVD)," commented the team from the University of Wisconsin-Madison, the University of Illinois at Urbana-Champaign and MicroLink Devices Inc.
 
This integration on silicon could lead to the development of chip scale, reliable and mass-producible photonic integrated circuits (PIC). The researchers contrast this with other integration methods such as wafer bonding: "Hybrid integration methods rely on precise alignment to achieve efficient waveguide to laser optical coupling, which in turn requires tight fabrication machining tolerances. Direct integration onto silicon through heteroepitaxy enables mid-infrared (IR) optoelectronic devices to be integrated with mature CMOS-compatible silicon platforms at low cost and high throughput."
 
Mid-infrared QCL is usually grown on indium phosphide (InP). The team paid particular attention to creating a virtual InP substrate on silicon by combining molecular beam epitaxy (MBE) and MOCVD. MOCVD is superior to MBE in production. "The remaining technical challenge is to overcome the defects and epitaxial growing-related problems caused by large lattice constant and thermal expansion mismatches (e.g., about 8% lattice mismatches) and about 50% thermal expansion coefficient mismatches between InP and primary substrates such as silicon," the researchers comment.
The arsenide portion of the template structure (Figure 1) is a limited company grown on a commercial (001) GaP/Si template (supplied by NAsP III/V) using a solid source MBE. The substrate is nominally coaxial and compatible with high-throughput industrial-scale CMOS electronics production. The initial layer consists of an Indium Gallium Arsenide (InGaAs) dislocation filter layer (DFL) sandwiched in GaAs. By keeping the thickness of the initial arsenide layer at 0.5 μm, the researchers sacrificed some of the potential for reducing the penetration dislocation density (TDD). The GaAs layer grows in two steps, first at low temperatures of 500°C and then at higher temperatures (580/610°C for the lower/upper layers, respectively). As far as the upper layers are concerned, one motivation for doing so is to avoid the escape of indium in InGaAs DFL.
 
The upper InP metaseptic buffer (MBL) portion of the template grows through MOCVD and includes four additional DFLS, consisting of three 2nm/37nm InAs/InP pairs.
 
The QCL is completed using MOCVD and has a total epitaxial thickness (including the metamorphic buffer layer and the laser layer) of approximately 13 μm. QCL/Si did not show cracks, which the team believes could be due to two factors: the small sample size of 1.7cmx1.7cm, and the curvature accumulation mitigated by the 800 μm thick silicon substrate. The TDD for the arsenide portion of the template was estimated to be 1.0 x109 / cm-2. InP MBL reduces this to 7.9x108 /cm 2.
Under pulsed operation, the threshold current density on silicon is 22% lower than that of devices grown on bulk InP substrates during the same process run: in the figure, 1.50kA/cm 2 and 1.92kA /cm 2, respectively. The researchers comment: "This may reflect reduced incorporation of silicon dopants within the active nuclear superlattices due to pre-existing defects or differences in the growth temperatures of the silicon and InP substrate surfaces. In addition, uneven growth around the defect site may reduce carrier mobility and tunneling efficiency, which would explain the higher series resistance observed in devices grown on silicon."
 
The higher the voltage required to provide a given current injection in a silicon-based QCL, the higher the series resistance. Despite the higher series resistance, silicon-based QCL also provides higher peak optical output power: 1.64W for silicon-based devices and 1.47W for INP-based devices. The corresponding slope efficiency is 0.72W/A and 0.65W/A, and the electro-optical conversion efficiency is 2.85% and 2.50%, respectively.
 
The emission spectral analysis showed a variety of modes in the wavelength range 7.6-8.3 μm. The maximum peak values of InP and Si based devices are about 8.1 μm and 8.0 μm, respectively. These wavelengths are slightly shorter than the design target of 8.2 μm. The researchers believe that this difference may be due to local growth changes affecting layer thickness, as shown in X-ray diffraction analysis.
 
Source: Laser Network
Σχετικές προτάσεις

  • Application of Multipurpose Femtosecond Laser Interferometry in High Precision Silicon Nanostructures

    Researchers from the Laser Processing Group of the IO-CSIC Institute of Optics in Spain report on the application of multi-purpose femtosecond laser interference in high-precision silicon nanostructures. The related research was published in Optics&Laser Technology with the title "Versatile femtosecond laser interference pattern applied to high precision nanostructured of silicon".Highlights:...

    2024-07-10
    Δείτε τη μετάφραση

  • Germany has developed direct laser welding technology to achieve adhesive free connection from fiber to chip

    Recently, researchers and their partners from the Fraunhofer Institute for Reliability and Microstructure (IZM) in Germany announced the successful development of a laser welding technology that can efficiently fix optical fibers onto photonic integrated circuits (PICs) without the need for adhesive bonding.This technology is developed in response to biophoton sensing technology, mainly utilizing ...

    2023-08-22
    Δείτε τη μετάφραση

  • CinIonic launches a new cinema screen specifically designed for laser theaters

    CinIonic announced the launch of a new cinema screen specifically designed for laser auditoriums. CinIonic Laser Screen 2.4 amplifies the power of laser projection by optimizing efficiency and enhancing screen presentation. This new screen is aimed at becoming the ideal companion for CinIonic Laser and is the first screen product in the CinIonic All Laser Solution portfolio.The CinIonic laser scre...

    2023-09-20
    Δείτε τη μετάφραση

  • Additive manufacturing of free-form optical devices for space use

    A group of researchers and companies are using the iLAuNCH Trailblazer program to develop and identify new optical manufacturing processes and materials for space flight applications, and demonstrating them in space cameras.The University of South Australia, together with SMR Australia and VPG Innovation, will utilize an emerging optical manufacturing technology called freeform optics, which is no...

    2023-12-04
    Δείτε τη μετάφραση

  • Progress has been made in the corrosion mechanism of alkali aluminum phosphate glass at Shanghai Optics and Machinery Institute

    Recently, the Advanced Laser and Optoelectronic Functional Materials Department of the Shanghai Institute of Optics and Precision Mechanics, Chinese Academy of Sciences, has made new progress in the corrosion mechanism of alkali aluminophosphate glass. The research findings were published in The Journal of Physical Chemistry C under the title "Formation Mechanism of Crystal Phase during Corrosion ...