Shanghai Photonics Corporation has made progress in laser welding of structural materials (Ni-28W-6Cr alloy) for new-generation molten salt reactors

987
2023-08-25 13:59:25
Посмотреть перевод

Recently, Yang Shanglu, a researcher at the Laser Intelligent Manufacturing Technology Research and Development Center of Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, has made new progress in laser welding of the fourth-generation reactor-molten salt reactor structural material Ni-28W-6Cr nickel-based superalloy. 

The research team applied the high power fiber laser welding technology to Ni-28W-6Cr alloy for the first time, and analyzed the dynamic cracking behavior characteristics of the laser welding hot crack by using high speed camera technology, and clarified the cracking mechanism. 

The relevant research results are summarized as "Dynamic laser welding hot cracking behavior and mechanism of new structural material Ni-28W-6Cr alloy for molten. salt reactor "was published in the Journal of Materials Research and Technology.

Ni-28W-6Cr high temperature nickel base alloy is a new structural material designed for the new generation of high temperature molten salt reactor (> 850℃) in China, which has excellent high temperature resistance and corrosion resistance to molten salt. However, due to the high alloying level of the alloy, it has a very high sensitivity to welding hot cracks, which poses a great threat to the service safety of welded joints and structures. 

In order to improve the laser welding quality of Ni-28W-6Cr alloy and promote the application of nuclear energy engineering, it is urgent to study the cracking behavior and influencing factors of Ni-28W-6Cr high temperature nickel base alloy laser welding, and solve the problem of laser cracking by elucidating the cracking mechanism.

The dynamic crack behavior of Ni-28W-6Cr alloy laser welding was analyzed by using a 10,000-watt laser processing unit combined with high-speed imaging technology, and the relationship between the type, number, size, propagation behavior and laser power of the hot crack was obtained. 

The influencing factors of hot crack initiation and propagation (laser process parameters, element segregation, precipitated phase and stress, etc.) were clarified, and the mechanism of hot crack cracking in laser welding was elucidated. The work laid a foundation for the control of Ni-28W-6Cr alloy laser welding hot crack, the realization of alloy defect free laser welding, and promote the construction of a new generation of molten salt reactor.

This work is supported by the National Natural Science Foundation Youth Fund and the National Key Research and Development Program.

Figure 1: (a) Dynamic cracking behavior of Ni-28W-6Cr alloy during laser welding; (b) microstructure of Ni-28W-6Cr alloy during laser welding.

Figure 2 EBSD analysis results of Ni-28W-6Cr alloy laser welding hot crack: (a) solidification crack, (b) liquefaction crack.

Source: Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences

Связанные рекомендации

  • Samsung and SK Hynix Explore Laser Debonding Technology

    According to South Korean media etnews, Samsung Electronics and SK Hynix have started the process technology conversion of high bandwidth memory (HBM) wafers, with the introduction of new technologies to prevent wafer warping as the core, which is considered to be aimed at the next generation HBM. It is expected that with the process transformation, the material and equipment supply chain will als...

    2024-07-16
    Посмотреть перевод

  • Polish and Taiwan, China scientists are committed to new 3D printing dental implants

    Researchers from Wroclaw University of Technology and Taipei University of Technology in China are developing dental implants made from 3D printed ceramic structures connected to metal cores. Due to the use of biodegradable magnesium, bone tissue will gradually grow into such implants."The result will be a composite implant that can replace human teeth. Its scaffold is made of aluminum oxide...

    2024-04-17
    Посмотреть перевод

  • Future oriented strategic technology: integrated manufacturing of large composite materials with additive and subtractive materials and its key elements

    Thermowood has developed a large-scale additive and subtractive material manufacturing equipment, LSAM, and successfully printed tooling molds on site that can be used for aerospace composite material forming, demonstrating its low-cost and rapid response to composite material manufacturing capabilities to the public.As a large-scale component additive manufacturer, Thermowood has developed a near...

    2024-04-19
    Посмотреть перевод

  • Mycronic receives first order after upgrading solid-state lasers

    Recently, Mycronic AB received its first order from SK Electronics in Japan to upgrade the installed display mask writer from a gas laser to a solid-state laser. The upgrade is scheduled to be delivered within the next two years.Image source: MycronicIt is reported that Mycronic's "Pattern Generators" department provides mask writers for display manufacturing and semiconductor production. So far, ...

    2023-10-16
    Посмотреть перевод

  • Progress has been made in the research of single shot characterization technology for complex combination laser pulses at Shanghai Institute of Optics and Fine Mechanics

    Recently, the research team of the High Power Laser Physics Joint Laboratory at the Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, has made significant progress in the study of single shot characterization technology for complex combination laser pulses. The research team utilized an improved broadband transient grating frequency resolved optical switch technology (T...

    03-24
    Посмотреть перевод